FEXA provides aluminium extrusion enterprises with different measure billets as well as alloys.
FEXA provides aluminium extrusion enterprises with different measure billets as well as alloys. Special measure billets and special alloys are produced according to the client's technical requirements. These ones are made with the highest raw material quality Available alloys and measures information Available dimensions: Diameters: 4", 5", 6" y 7" (Inches) Longitude: starting from 400 mm . in multiples of 50 mm . * Homogenized according to the consumption necessities. Download the printable version of the alloys table MS Word Document (. doc) - Size: 122 Kb. Aluminum Extrusion Alloys: Number and Characteristics Major Alloying Elements Temper and Thickness (inches) Tensile Strength- ksi Elongation Percentmin. in 2 in. Or 4D Ultimate Yield Min. Max. Min. Max. 1060 Softest alloy available. Primarily used for sheating tube for the wire and cable industry. 99, 6 % min. - 0 ALL 8, 5 14, 0 2, 5 & 25 Aluminum - H112 ALL 8, 5 & 2, 5 & 25 1100 Co mm ercially pure aluminium. Used in a variety of aplications where stregth is not a priority. Corrosion resistant and formable. Can be anodized and polished. 99 % min. - 0 ALL 11, 0 15, 5 3, 0 & 25 AluminumCu, 05- 0, 20 - H112 ALL 11, 0 & 3, 0 & & 1050 Developed especially for electrical conductor use with a minimum conductivity of 61- 62 % IACS. Used in both solid and tubular forms. 99, 5 % min. - 0 0, 375 - 1, 000 8, 5 14, 0 & & & Aluminum - H111 ALL 8, 5 & 3, 5 & 6005 Similar to 6061 alloy. Used in structural applications. Si 0. 6- 0. 9Mg 0. 4- 0. 6 - T1 Up thru 0. 500 25. 0 & 15. 0 & 16 - T5 Up thru 0. 124 38. 0 & 35. 0 & 8 0. 125- 1. 000 38. 0 & 35. 0 & 10 6060 Has beter extrudability than 6063. The minimum mechanical proprieties (with the exception of minimum welded proprieties) , response to finishim process and corrosion resistance are similar to 6063 Si . 30- 0. 6Mg 0. 35- 0. 6 - T51 Up thru 0. 125 22. 0 & 16. 0 & 8 Up thru 1. 000 22. 0 30. 0 16. 0 25. 0 8 - T61 Up thru 0. 124 30. 0 & 25. 0 & 8 0. 125- 1. 000 30. 0 & 25. 0 & 10 6061 Most versatile of heat- treatable group. Will take considerable forming in T4. Good corrosion resistance. Used in transportation and structural applications. Mg 0. 8- 1. 2Si 0. 40- 0. 8 - 0 ALL & 22. 0 & 16. 0 16 - T1 Up thru 0. 625 26. 0 & 14. 0 & 16 - T4, T4510 and T4511 ALL 26. 0 & 16. 0 & 16 - T42 ALL 26. 0 & 12. 0 & 16 - T51 Up thru 0. 625 35. 0 & 30. 0 & 8 - T6, T62, T6510 and T6511 Up thru 0. 249 38. 0 & 35. 0 & 8 0. 250 and over 38. 0 & 35. 0 & 10 6063 The most popular extrusion alloy. Takes a good surface finish, is corrosion- resistant, and can be heat- treated for strength. Mg 0. 45- 0. 9Si 0. 20- 0. 6 - 0 ALL & 19. 0 & & 18 - T1 Up thru 0. 500 17. 0 & 9. 0 & 12 0. 501- 1. 000 16. 0 & 8. 0 & 12 - T4 and T42 Up thru 0. 500 19. 0 & 10. 0 & 14 0. 501- 1. 000 18. 0 & 9. 0 & 14 - T5 Up thru 0. 500 22. 0 & 16. 0 & 8 0. 501- 1. 000 21. 0 & 15. 0 & 8 - T52 Up thru 1. 000 22. 0 30. 0 16. 0 25. 0 8 - T6 and T62 Up thru 0. 124 30. 0 & 25. 0 & 8 0. 125- 1. 000 30. 0 & 25. 0 & 10 6101 High strength bus conductors, good extrudability, weldability, brazeability, good resistance to stress corrosion craking with average machinability. Si 0. 30- 0. 7Mg 0. 35- 0. 8 - T6 0. 125- 0. 500 29. 0 & 25. 0 & 15 - T61 0. 125- 0. 749 20. 0 & 15. 0 & 19 0. 750- 1. 499 18. 0 & 11. 0 & 19 1. 500- 2. 000 15. 0 & 8. 0 & 19 - T63 0. 125- 1. 000 27. 0 & 22. 0 & 17 - T64 0. 125- 1. 000 15. 0 & 8. 0 & 20 - T65 0. 125- 0. 749 25. 0 32. 0 20. 0 27. 0 & 6105 Good medium to high strength with average machinability and good corrosion resistance Si 0. 60- 0. 10Mg 0. 45- 0. 80 - T1 Up thru 0. 500 25. 0 & 15. 0 & 16 - T5 Up thru 0. 500 38. 0 & 35. 0 & 8 6262 Best machining of all extrusion alloys. Good corrosion resistance. Mg 0. 80- 1. 2Si 0. 40- 0. 80Pb 0. 4- 0. 7Bi 0. 40- 0. 70 - T6, T62, T6510 and T6511 ALL 38. 0 & 35. 0 & 10 6351 Similar to 6061 alloy. Used in structural applications. Will take considerable forming in T4. Good corrosion resistance. Used in transportation and general structures. Si 0. 70- 1. 3Mg 0. 40- 0. 80Mn 0. 40- 0. 80 - T1 Up thru 0. 499 26. 0 & 13. 0 & 15 - T4 Up thru 0. 749 32. 0 & 19. 0 & 16 T5 Up thru 0. 249 38. 0 & 35. 0 & 8 0. 250- 1. 000 38. 0 & 35. 0 & 10 T51 0. 125- 1. 000 36. 0 & 33. 0 & 10 T54 Up thru 0. 500 30. 0 & 20. 0 & 10 T6 Up thru 0. 124 42. 0 & 37. 0 & 8 0. 125- 0. 749 42. 0 & 37. 0 & 10 6463 Designed to accept a bright finish through anodizing or polishing. Decorative trim applications; machinable andheat- treatable. Mg 0. 45- 0. 90Si 0. 20- 0. 60High purity versionof 6063 T1 Up thru 0. 500 17. 0 & 9. 0 & 12 T5 Up thru 0. 500 22. 0 & 16. 0 & 8 T6 and T62 Up thru 0. 124 30. 0 & 25. 0 & 8 0. 125- 0. 500 30. 0 & 25. 0 & 10
