FIRE CLAY AND HIGH ALUMINA CASTABLES

FIRE CLAY AND HIGH ALUMINA CASTABLES

FIRE CLAY AND HIGH ALUMINA CASTABLES Brand Al2o3 % Min Fe2o3 % Max PCE Orton MAX (Service) Temp BD After Casting & drying at 110 degree Grain size mm Water reqd. for casting C. C. S. At 110 Degree Kg / Cm2 C. C. S. AT Service Temp Kg / Cm2 AMPL- DENSE- CAST 36 4 - 1300 2. 0 0. 5 16- 17 300- 400 300- 400 AMPL- CAST- 38 38- 40 4 - 1350 1. 8- 2. 0 0. 5 16- 17 200- 300 150- 200 AMPL- CAST- 45 42- 44 4 - 1400 2. 0- 2. 2 0. 5 16 200- 300 150- 200 AMPL- CAST- 45 44- 96 5 - 1400 2. 1- 2. 2 0. 5 16 300- 400 250- 350 AMPL- CRETE 50 5 20- 23 1400 2. 1- 2. 2 0. 5 16 250- 350 200- 300 AMPL- CRETE- SUPER 70 6 30- 31 1450 2. 3- 2. 5 0. 5 16 300- 400 400- 500 AMPL- CAST- 1500 50 1. 5 28- 29 1500 2. 1- 2. 2 0. 5 12- 14 250- 350 - AMPL- CAST- 1600 60 1. 0 31- 32 1600 2. 2- 2. 3 0. 5 12 250- 350 - NOTE : Thermal Conductivity ? Pre fired hot face 500 degree C. Above are average Test Data subjected to reasonable variation. Return to Previous Page