Place of Origin: Jiangsu China (Mainland) Brand Name: Fenghua Model Number: inconel 600
Application: wide application Shape: wire, bar, strip, pipe Material: alloy
Dimensions: wide range Chemical Composition: Ni Cr Fe Cu Mn C Si S
Packaging & Delivery
Packaging Detail : Wooden case
Delivery Detail 30 days
Grade: MONEL 400, INCONEL 600, INCONEL 601, INCONEL 625
INCOLOY 800, INCOLOY 800H, INCOLOY 825
Form: wire, strip, bar, tube
Inconel 600 is a standard engineering material for applications which require resistance to corrosion and heat. The alloy also has excellent mechanical properties and presents the desirable combination of high strength and good workability. Inconel 600
Inconel 600 Chemical composition: Alloy% NiCrFeCMnSiCuPS
600Min. 72146
Max. 17100. 1510. 50. 50. 0150. 015
Inconel 600 Physical properties: Density8. 4 g/ cm?
Melting Point1370- 1425
Inconel 600 Alloy m inimum Mechanical properties in the room temperature: Aolly statusTensile strength
Rm N/ mm ?Yield strength
R P 0. 2N/ mm ?Elongation
A 5 % Brinell hardness
HB
Annealing treatment55024030?195
Solution treatment50018035?185
Inconel 600 Metallurgical structure
600 is face- centered cubic lattice structure.
Inconel 600 Corrosion resistance
600 have corrosion resistance to many kinds of corrosive media. Chromium content made it with better corrosion resistance than Nickel 99. 2 (alloy200) and Nickel 99. 2 ( alloy201, low carbon) in the oxidize environment. Meantime, high Nickel content make this alloy with good corrosion resistance in the reduction condition and alkaline solution, and also effective avoid chlorine- iron stress corrosion cracking. 600 have good corrosion resistance in the acid, acetic acid, formic acid, stearic acid and other organic acid, with medium corrosion resistance in the inorganic acid. The alloy with excellent corrosion resistance in the first and the second recycling use of the high purity water in the nuclear reactor. Especially excellent corrosion resistance to dry chlorine and chlorine hydride applied up to 650 . When nder the high temperature, annealing and state solution alloy have good antioxidant off and high- intensity in the air, 600 can resist the a mm onia, nitriding and carburizing atmosphere, but at the turn of the changes in redox conditions, it will be corrosion by parts of oxidation media. ( such as green death liquid)
Inconel 600 Application field
1. Erosion thermocouple sheath of the atmosphere
2. Vinyl chloride monomer production: corrosion resistance to chlorine, hydrogen chloride, oxidation and carbonation.
3. Oxide shaft chloride converted to six fluoride: hydrogen fluoride anti- corrosion.
4. Corrosive alkali metal produce and usage filed, especially the sulfide use environment.
5. Use Chlorine produce titanium dioxide
6. Organic or inorganic chlorine produce: corrosion resistance to chlorine and fluoride.
7. Nuclear reactor
8. Heat treatment furnace flask and components, especially in the carbonization and nitride atmosphere.
9. Petrochemical works production of catalytic regeneration in the application of more than 700 reco mm ended the use of 600, in order to obtain a longer service life.